牌號(hào) Brand | 組成 Consist Of | 分子量 Average Molecular | 熔點(diǎn) Tm (oC) | 玻璃化轉(zhuǎn)變溫度 Tg (oC) | 產(chǎn)品特點(diǎn) Performance |
XCP-3000H | AA/HDO | 3000 | 55 | 縮短開放時(shí)間，降低熔融粘度，提高初始強(qiáng)度 shortens open time, lowers melt viscosity, increases initial strength
| |
FLP-3500H | 3500 | 55 | |||
XCP-R4500H | 4500 | 55 | |||
XCP-R8500HA | 8500 | 57 | |||
NOTP-3870-A3 | DDA/HDO | 3500 | 70 | ||
CTP-44 | AA/BDO | 2000 | 50 | 提高強(qiáng)度，降低使用溫度范圍 increases strength, lowers application temperature | |
XCP-TM3000B | 3000 | 55 | |||
FLP-2000N | AA/NPG | 2000 | -48 | 提高柔軟度，提高耐溶劑性 increases flexibility, improves solvent resistance | |
PES-2000NB | AA/NPG/BDO | 2000 | -58 | 提高柔軟度，提高耐水解性 increases flexibility, improves hydrolysis resistance | |
PES-2200NH | AA/NPG/HDO | 2000 | -60 | ||
CTP-244 | AA/EG/BDO | 2000 | -62 | ||
XCP-R2170 | - | 4000 | -15 | 延長(zhǎng)開放時(shí)間，提高柔軟度，降低熔融粘度，提高對(duì)非極性表面的粘結(jié)性 extends open time, increases flexibility, lowers melt viscosity, improves adhesion to non-polar (low energy) substrates | |
XCP-R2370 | - | 4000 | -30 | ||
XCP-R2570 | - | 5500 | -55 | ||
FLP-PA1000N | PA/NPG | 1000 | 26 | 提高熔融粘度，提高初始強(qiáng)度，提高對(duì)極性表面的粘結(jié)性 increases melt viscosity, increases initial strength, improves adhesion to polar substrates | |
XCP-R3170 | - | 3000 | 30 | ||
XCP-R5170 | - | 2600 | 50 | ||
XCPA-2000HL | PA/HDO | 2000 | -15 | 延長(zhǎng)固化時(shí)間，降低熔融粘度，提高對(duì)非極性表面的粘結(jié)性 extends set time, lowers melt viscosity，improves adhesion to non-polar (low energy) substrates | |
XCP-2000IPS | - | 2000 | -22 | 提高耐水解性，提高耐溫性 improves hydrolysis resistance, improves thermal stability |
產(chǎn)品搜索
產(chǎn)品分類
PUR用聚酯多元醇
產(chǎn)品介紹
旭川化學(xué)為熱熔膠聚氨酯提供高品質(zhì)和種類豐富的聚酯多元醇原料。結(jié)晶型聚酯多元醇可以提供優(yōu)異的機(jī)械強(qiáng)度、耐化學(xué)和溶劑性能、廣泛的粘結(jié)適用性。無定形聚酯多元醇能提供出色的表面浸潤(rùn)性、初始粘接強(qiáng)度、和耐磨等性能。